UNS: G10600-10900 DIN: 1.1231-1.1248 GB: 65Mn, 70Mn 탄성 계수: 206843 권장 최대 작동 온도: 121°C 주원소 화학 성분(wt%): C0.65 - 0.98%, Mn 0.30 -

UNS: G10600-10900 DIN: 1.1231-1.1248 GB: C58D-C88D 탄성 계수: 206843 권장 최대 작동 온도: 121 °C 주요 원소 화학 성분(wt%): C 0.55 - 0.88, Mn 0.40-0.90%

UNS: N05500 DIN: 2.4375 GB: 68Ni28Cu28Al Modulus of elasticity: 179140 Recommended maximum operating temperature: 287 °C Main element chemical composition (wt%)：Ni 63.0 min%, Cu 27.0 -33.0%,

UNS: N04400 DIN: 2.436 GB: 68Ni28Cu28Fe Elastic modulus: 179140 Recommended maximum operating temperature: 232°C Main element chemical composition (wt%) : Ni 63.0min %, Cu 28.0-34.0% Description

UNS: N10276 DIN: 2.4819 GB: NS3304 Elastic modulus: 211523 Recommended maximum operating temperature: 371°C Major element chemical composition (wt %) : 51.0 63.5% Ni, Cr 14.5

UNS: N07718 DIN: 2.4668 GB: GH4169 탄성 계수: 204085 권장 최대 작동 온도: 704°C 주요 원소 화학 성분(wt%) : Ni 50.0-55.0%, Cr 17.0-21.0%, Fe11.0-24.0% 설명

UNS: N07750 DIN: 2.4669 GB: GH4145 탄성 계수: 213737 권장 최대 작동 온도: 371(538)°C 주요 원소 화학 성분 (wt%) : Ni70.0분 %, Cr 14.0-17.0%, Fe 5.0-9.0%

UNS: S66286 DIN: 1.498GB: GH2132 탄성 계수: 213737 권장 최대 작동 온도: 538°C 주요 원소 화학 성분(wt %) : NI 24-27%, 13.5 16.0% Cr,