UNS: G10600-10900 DIN: 1.1231-1.1248 GB: 65Mn、70Mn Modulus of elasticity: 206843 Recommended maximum operating temperature: 121 °C Main element chemical composition (wt%)：C0.65 – 0.98%, Mn 0.30 –

UNS: G10600-10900 DIN: 1.1231-1.1248 GB: C58D-C88D Modulus of elasticity: 206843 Recommended maximum operating temperature: 121 °C Main element chemical composition (wt%)：C 0.55 – 0.88, Mn 0.40-0.90%

UNS: N05500 DIN: 2.4375 GB: 68Ni28Cu28Al Modulus of elasticity: 179140 Recommended maximum operating temperature: 287 °C Main element chemical composition (wt%)：Ni 63.0 min%, Cu 27.0 -33.0%,

UNS: N04400 DIN: 2.436 GB: 68Ni28Cu28Fe Elastic modulus: 179140 Recommended maximum operating temperature: 232°C Main element chemical composition (wt%) : Ni 63.0min %, Cu 28.0-34.0% Description

UNS: N10276 DIN: 2.4819 GB: NS3304 Elastic modulus: 211523 Recommended maximum operating temperature: 371°C Major element chemical composition (wt %) : 51.0 63.5% Ni, Cr 14.5

UNS : N07718 DIN : 2.4668 GB : GH4169 Module d'élasticité : 204085 Température de fonctionnement maximale recommandée : 704°C Composition chimique des éléments principaux (wt%) : Ni 50.0-55.0%, Cr 17.0-21.0%, Fe11.0-24.0% Description

UNS : N07750 DIN : 2.4669 GB : GH4145 Module d'élasticité : 213737 Température de fonctionnement maximale recommandée : 371(538)°C Composition chimique de l'élément principal (wt%) : Ni70.0min %, Cr 14.0-17.0%, Fe 5.0-9.0%

UNS : S66286 DIN : 1.498 GB : GH2132 Module d'élasticité : 213737 Température de fonctionnement maximale recommandée : 538°C Composition chimique des principaux éléments (poids %) : NI 24-27%, 13.5 16.0% Cr,